R60702 zirconium yeeb nkab
R60702 tau cais raws li American txheem zirconium, zirconium raj ua tiav kev ua tiav Cov Lus Qhia Tshwj Xeeb: ASTM B551 / B551M-2012.
R60702 Zirconium Cov yam ntxwv: Zirconium yog cov hlau tsis tshua muaj, zoo nkauj heev thiab lwm yam kev ua tub rog, ua tub rog, nomic zog teb.
R60702 Zirconium Pab: Zirconium yog cov khoom tseem ceeb hauv kev tsim khoom xws li tso tsheb hlau luam, tso tsheb hlau luam, cannons thiab banomroof daim hlau.
zirconium R60702 Yeeb Yam Khoom Sib xyaw
| Zirconium qib |
ZR 702 |
ZR 700 |
ZR705 |
| Tsis yog |
R60702 |
R60704 |
R60705 |
| Zirconium + Hafnium (min) |
99.2 |
97.5 |
95.5 |
| Hafnium (Max |
4.5 |
4.5 |
4.5 |
| Hlau + chromium |
0.2 max |
0.2-0.4 |
0.2 max |
| Lub thoob |
- |
1.0-2.0 |
- |
| Hydrogen (Max) |
0.005 |
0.005 |
0.005 |
| Nitrogen (max) |
0.025 |
0.025 |
0.025 |
| Carbon (max) |
0.05 |
0.05 |
0.05 |
| Niobium |
- |
- |
2.0-3.0 |
| Cov pa (max) |
0.16 |
0.18 |
0.18 |
R60702 zirconium raj neeg siv khoom
| Cov Khoom Siv Lub Cev |
Me me |
Askiv |
Lus |
| Ceev |
6.5 G / CC |
0.235 lb / hauv3 |
|
| Cov Khoom Siv Neeg Kho Tshuab |
| Hardness, Rockwell A |
49 |
49 |
Kwv yees los ntawm cov vickers |
| Hardness, Rockwell B |
78 |
78 |
Kwv yees los ntawm cov vickers |
| Hardness, vickers |
150 |
150 |
Annealed qauv |
| Tensile lub zog, qhov kawg |
Min 379 mpa |
Min 55000 psi |
|
| Tensile lub zog, tawm los |
Min 207 mpa |
Min 30000 PSI |
0.2% ys |
| Elongation thaum so |
16 % |
16 % |
Hauv 50 hli |
| Modulus ntawm elasticity |
99.3GPA |
14400 Ksi |
|
| Poisson tus piv |
0.35 |
0.35 |
|
| Qaug zog muaj zog |
125 MPa |
18100 psi |
5 e {+5 cmles, tsis yog |
| Qaug zog muaj zog |
145 MPa |
21000 psi |
3 e {+7 cmles, tsis muaj hnub nyoog |
| Qaug zog muaj zog |
MPA |
25400 PSI |
5 e {{+3 cmles, tsis muaj hnub nyoog |
| Qaug zog muaj zog |
60 MPA |
8700 PSI |
3 e {+7 cmles, thached |
| Shear Modulus |
36.2 GPA |
5250 Ksi |
|
| Cov Khoom Siv Hluav Taws Xob |
| Hluav taws xob tiv thaiv hluav taws xob |
3.97E - 005 Ohm-Cm |
3.97E - 005 Ohm-Cm |
Temp Coefficient yog 0.0044 /℃ntawm 20 degree |
| Sib Nqus Tau |
1.34E-06 |
1.34E-06 |
CGS / g; ntshiab zr |
| Qhov tseem ceeb sib nqus teb lub zog, oersted |
47 |
47 |
Ntshiab zr |
| Tseem ceeb heev superconducting kub |
0.595 - 0.625 K |
0.595 - 0.625 K |
ntshiab zr |
| Thermal Khoom |
| Tshav kub ntawm fusion |
250 J/g |
108 BTU / LB |
|
| CTE, Linear 20 degree |
5.89 μm / m -} degree |
3.27 μin / in {-℃f |
Thaum 25 degree |
| CTE, Linear 250 Qib |
6.3 μm / m -} degree |
3.5 μin / in -}℃f |
|
| CTE, linear 500 degree |
6.9 μm / m -} degree |
3.83 μm / in -}℃f |
|
| Kev Kub Loj Tshaj |
0.285 j / g -} degree |
0.0681 btu / lb -℃f |
|
| Thermal conductivity |
22 W/m-K |
153 btu - hauv / hr - ft2-℃f |
|
| Melting taw tes |
1852 Qib |
3370℃f |
|
| Kho qhov muag |
| Emissivity (0-1) |
0.32 |
0.32 |
650 nm; unoxidized dawb zr qauv; tag nrho |
|
Zirconium R60702 raj cov khoom lag luam duab
Gnee Pab Pawg Neeg Siv Khoom Mus Xyuas
Peb muaj kev tshaj lij kev pab cuam online cov neeg ua haujlwm. Yog tias koj muaj lus nug txog R60702 zirconium yeeb nkab, thov xa rau peb thiab peb yuav teb rau koj hauv ib hnub ua haujlwm.
Cim npe nrov: R60702 zirconium yeeb nkab, Tuam Tshoj R60702 zirconium yeeb nkab tshuab tsim khoom, cov chaw muag khoom, Hoobkas